# J. Amodeo, Thu Feb 26 10:51:45 CET 2015
# MgO single cristal CRSS versus temperature data, 100 slip planes
# Pressure = 100GPa, strain rate = 1e-16 /s, dislocation density = 1e12 m^{-2}
# If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Cordier et al. Nature 2012
# T [K] CRSS [MPa]
0 920
100 834
200 749
300 667
400 589
500 515
600 446
700 382
800 323
900 269
1000 220
1100 176
1200 138
1300 104
1400 76
1500 53
1600 34
1700 21
1800 11
1900 5
2000 2
2100 0