# J. Amodeo, Thu Feb 26 10:51:45 CET 2015 # MgO single cristal CRSS versus temperature data, 100 slip planes # Pressure = 100GPa, strain rate = 1e-2 /s, dislocation density = 1e12 m^{-2} # If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Cordier et al. Nature 2012 # T [K] CRSS [MPa] 0 920 100 890 200 858 300 827 400 796 500 765 600 735 700 706 800 676 900 648 1000 620 1100 592 1200 565 1300 539 1400 513 1500 488 1600 464 1700 440 1800 417 1900 395 2000 373 2100 352 2200 332 2300 313 2400 294 2500 276 2600 258 2700 242 2800 226 2900 210 3000 196 3100 182 3200 168 3300 156 3400 144 3500 132 3600 121 3700 111 3800 102 3900 93 4000 84 4100 77 4200 69 4300 63 4400 56 4500 51 4600 45 4700 41 4800 36 4900 32 5000 28 5100 25 5200 22 5300 19 5400 17 5500 15 5600 13 5700 11 5800 10 5900 8 6000 7 6100 6 6200 5 6300 5 6400 4 6500 3 6600 3 6700 3 6800 2 6900 2 7000 2 7100 1 7200 1 7300 1 7400 1 7500 1 7600 1 7700 1 7800 1 7900 0