# J. Amodeo, Thu Feb 26 10:51:45 CET 2015 # MgO single cristal CRSS versus temperature data, 110 slip planes # Pressure = 100GPa, strain rate = 1e-6 /s, dislocation density = 1e12 m^{-2} # If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Cordier et al. Nature 2012 # T [K] CRSS [MPa] 0 1950 100 1859 200 1762 300 1664 400 1567 500 1471 600 1377 700 1285 800 1196 900 1109 1000 1026 1100 945 1200 867 1300 793 1400 722 1500 654 1600 590 1700 530 1800 473 1900 419 2000 370 2100 324 2200 281 2300 242 2400 207 2500 175 2600 146 2700 121 2800 98 2900 79 3000 63 3100 49 3200 37 3300 28 3400 20 3500 15 3600 10 3700 7 3800 5 3900 3 4000 2 4100 1 4200 1 4300 1 4400 0