# J. Amodeo, Tue Mar 17 15:51:52 CET 2015 # MgO single cristal CRSS versus temperature data, 110 slip planes # Pressure = 100GPa, strain rate = 1e-16 /s, dislocation density = 1e8 m^{-2} # If using this data set, please cite Cordier et al. Nature 2012 and Amodeo et al. PEPI 2015 # T [K] CRSS [MPa] 0 1950 100 1795 200 1632 300 1472 400 1317 500 1169 600 1028 700 894 800 770 900 654 1000 548 1100 451 1200 364 1300 287 1400 220 1500 163 1600 116 1700 78 1800 48 1900 27 2000 14 2100 6 2200 2 2300 1 2400 0