# J. Amodeo, Tue Mar 17 15:51:52 CET 2015
# MgO single cristal CRSS versus temperature data,  110 slip planes
# Pressure = 100GPa, strain rate = 1e-4 /s, dislocation density = 1e8 m^{-2}
# If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Amodeo et al. Phil Mag 2012

# T [K]     CRSS [MPa]
0 1950
100 1890
200 1826
300 1761
400 1695
500 1630
600 1565
700 1501
800 1437
900 1375
1000  1313
1100  1253
1200  1193
1300  1135
1400  1078
1500  1023
1600  969
1700  916
1800  865
1900  816
2000  768
2100  721
2200  676
2300  633
2400  591
2500  551
2600  513
2700  476
2800  441
2900  408
3000  376
3100  346
3200  318
3300  291
3400  265
3500  241
3600  219
3700  198
3800  179
3900  161
4000  144
4100  129
4200  114
4300  101
4400  90
4500  79
4600  69
4700  61
4800  53
4900  46
5000  40
5100  34
5200  29
5300  25
5400  22
5500  18
5600  16
5700  13
5800  11
5900  9
6000  8
6100  7
6200  6
6300  5
6400  4
6500  3
6600  3
6700  2
6800  2
6900  2
7000  2
7100  1
7200  1
7300  1
7400  1
7500  1
7600  1
7700  1
7800  0