# J. Amodeo, Thu Feb 26 10:51:45 CET 2015 # MgO single cristal CRSS versus temperature data, 100 slip planes # Pressure = 30GPa, strain rate = 1e-8 /s, dislocation density = 1e12 m^{-2} # If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Cordier et al. Nature 2012 # T [K] CRSS [MPa] 0 750 100 661 200 568 300 477 400 393 500 315 600 275 700 238 800 203 900 172 1000 144 1100 119 1200 96 1300 77 1400 60 1500 46 1600 34 1700 24 1800 16 1900 11 2000 6 2100 4 2200 2 2300 1 2400 0