# J. Amodeo, Tue Mar 17 15:51:53 CET 2015
# MgO single cristal CRSS versus temperature data,  100 slip planes
# Pressure = 30GPa, strain rate = 1e-2 /s, dislocation density = 1e8 m^{-2}
# If using this data set, please cite Cordier et al. Nature 2012 and Amodeo et al. PEPI 2015

# T [K]     CRSS [MPa]
0 750
100 715
200 676
300 637
400 598
500 559
600 521
700 484
800 448
900 413
1000  379
1100  347
1200  316
1300  295
1400  278
1500  262
1600  247
1700  232
1800  218
1900  204
2000  191
2100  178
2200  166
2300  155
2400  144
2500  134
2600  124
2700  115
2800  106
2900  98
3000  90
3100  83
3200  76
3300  70
3400  64
3500  58
3600  53
3700  48
3800  44
3900  40
4000  36
4100  32
4200  29
4300  26
4400  24
4500  21
4600  19
4700  17
4800  15
4900  14
5000  12
5100  11
5200  10
5300  9
5400  8
5500  7
5600  6
5700  5
5800  5
5900  4
6000  4
6100  3
6200  3
6300  3
6400  2
6500  2
6600  2
6700  2
6800  2
6900  1
7000  1
7100  1
7200  1
7300  1
7400  1
7500  1
7600  1
7700  1
7800  1
7900  1
8000  1
8100  0