# J. Amodeo, Thu Feb 26 10:51:45 CET 2015 # MgO single cristal CRSS versus temperature data, 100 slip planes # Pressure = 60GPa, strain rate = 1e-12 /s, dislocation density = 1e12 m^{-2} # If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Cordier et al. Nature 2012 # T [K] CRSS [MPa] 0 750 100 638 200 535 300 468 400 416 500 367 600 321 700 278 800 238 900 202 1000 169 1100 139 1200 112 1300 88 1400 68 1500 51 1600 36 1700 25 1800 16 1900 9 2000 5 2100 2 2200 1 2300 0