# J. Amodeo, Thu Feb 26 10:51:46 CET 2015 # MgO single cristal CRSS versus temperature data, 110 slip planes # Pressure = 60GPa, strain rate = 1e-6 /s, dislocation density = 1e12 m^{-2} # If using this data set, please cite Amodeo et al. Acta Materialia 2011 and Cordier et al. Nature 2012 # T [K] CRSS [MPa] 0 1300 100 1219 200 1135 300 1051 400 969 500 889 600 812 700 737 800 666 900 599 1000 534 1100 474 1200 417 1300 363 1400 314 1500 269 1600 228 1700 190 1800 157 1900 127 2000 101 2100 79 2200 60 2300 44 2400 32 2500 22 2600 15 2700 10 2800 6 2900 4 3000 2 3100 1 3200 1 3300 0